POLYGLASS
BANDING TAPE (also know as
Resiglass Armature Banding Tape)
|
|
|
Table I
| Curing Cycle * : |
| Time (hours) |
5 |
20 |
| Temperature (°C) |
150 |
100 |
*Recommended curing cycle for POLYGLASS TAPE
is 5 Hrs at 150 °C after the body attains temperature.
Table II
| Storage Temperature : |
| Storage Temperature (°C) |
15 |
20 |
| Time (months) |
12 |
6 |
Table III
Characteristics of New High Strength Polyglass Banding Tape- As Supplied
| Characteristics |
Unit |
Value |
| Thickness |
mm |
app. 0.33 |
| Weight (Mass) per 100m of 10 mm tape |
kg |
app. 0.56 |
| Resin Content |
% |
27 ± 2 |
| Yarn/cm width |
nos. |
30 ± 1 |
| Tolerance on tape width |
% |
± 10 |
| Tensile strength (for 20 mm width tape) |
kg |
500 |
| Maximum pull during banding |
kg/cm |
100 |
| Recommended curing cycle at 150 °C |
hours |
5 |
| Shelf Life (when kept below 15 °C in original packing) |
month |
12 |
| Weight Loss (after keeping at 200°C for 400 Hours) |
% |
10(Max) |
| Koeffler's Softening point of Resin |
°C |
200(Max) |
Table IV
Characteristics of New High Strength Polyglass Banding Tape -After Application & Curing
| Characteristics |
Unit |
Value |
| Maximum temperature withstand |
°C |
200 |
| Cured tape thickness (approx.) |
mm |
0.25 |
Tensile strength referred to each layer of tape
at room temperature
at 150 °C (after heat ageing - 10 days at 200 °C)
|
kg/cm
kg/cm
|
265
185
|
Elongation at break
at 20 °C
at 200 °C
|
%
%
|
1.6(Max)
2.0(Max)
|
Modulus of elasticity referred to total Cross Section of tape
at 20 °C
at 200 °C
|
kg/mm
kg/mm
|
6000
5000
|
| Arc Resistance |
second |
> 120 |
|
Available in Width:
8
mm, 10 mm, 20 mm, 25 mm, 30 mm, 40 mm, 50 mm, 100 mm. Other width on
request.
<<